http://repositorio.utfpr.edu.br/jspui/handle/1/37219| Título: | Estudo de caso: elaboração da curva de revenimento de uma liga fundida de aço do tipo E |
| Título(s) alternativo(s): | Case study: preparation of the tempering curve of a type E cast alloy steel |
| Autor(es): | Zangiacomo, Renan Chil |
| Orientador(es): | Tramontin, Sandra Mara Kaminski |
| Palavras-chave: | Aço - Tratamento térmico Metais - Propriedades mecânicas Aço fundido Steel - Heat treatment Metals - Mechanical properties Steel castings |
| Data do documento: | 5-Set-2024 |
| Editor: | Universidade Tecnológica Federal do Paraná |
| Câmpus: | Ponta Grossa |
| Citação: | ZANGIACOMO, Renan Chil. Estudo de caso: elaboração da curva de revenimento de uma liga fundida de aço do tipo E. 2024. Trabalho de Conclusão de Curso (Bacharelado em Engenharia Mecânica) - Universidade Tecnológica Federal do Paraná, Ponta Grossa, 2024. |
| Resumo: | Com a crescente demanda de produção de peças de aço-E em uma empresa de fundição, fez-se necessário o estudo de caso de um dos processos fabris empregados: o tratamento térmico de revenimento pós-têmpera e suas variações de temperatura. Neste trabalho foi elaborada uma curva de revenimento para o aço tipo E, na faixa de temperatura de 550ºC a 630ºC, com um intervalo de temperatura de 10°C, pelo tempo de duas horas cada tratamento. Para a confecção da curva de revenimento, foram utilizados corpos de provas que normalizados a 920ºC por 3 horas com rampa de aquecimento de 150ºC, temperados a partir de 900ªC com taxa de aquecimento igual ao da normalização e, posteriormente, revenido para elaborar a curva de dureza versus temperatura. A dureza foi obtida através de teste de dureza Brinell realizado no durômetro portátil Kingtester. |
| Abstract: | With the growing demand for E-grade steel components in a foundry, a detailed case study was conducted on one of the critical manufacturing processes: post-quenching tempering heat treatment and its temperature variations. This study aimed to develop a tempering curve for E-grade steel within a temperature range of 550°C to 630°C, with a 10°C interval for each treatment, and a treatment duration of two hours. To construct the tempering curve, test specimens were first normalized at 920°C for 3 hours with a heating ramp rate of 150°C per hour. Following normalization, the specimens were quenched from 900°C with the same heating rate as used during normalization. Subsequently, the specimens were tempered at various temperatures to generate the hardness versus temperature curve. Hardness measurements were performed using the Brinell hardness test with a portable Kingtester durometer. The resulting tempering curve provides valuable insights into the relationship between tempering temperature and hardness for E-grade steel components. |
| URI: | http://repositorio.utfpr.edu.br/jspui/handle/1/37219 |
| Aparece nas coleções: | PG - Engenharia Mecânica |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| curvarevenimentoacofundido.pdf | 201,96 kB | Adobe PDF |  Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.