http://repositorio.utfpr.edu.br/jspui/handle/1/181| Título: | Influência de parâmetros do processo FCAW-G nas características da solda do aço ASTM A-36 |
| Autor(es): | Rodrigues, Emanuel Rezende |
| Orientador(es): | Schiefler Filho, Marcos Flávio de Oliveira |
| Palavras-chave: | Engenharia mecânica Soldagem Aço - Soldagem Soldagem com arame tubular Mechanical Engineering Welding Steel - Welding Welding with cored wire |
| Data do documento: | 25-Fev-2010 |
| Editor: | Universidade Tecnológica Federal do Paraná |
| Câmpus: | Curitiba |
| Citação: | RODRIGUES, Emanuel Rezende. Influência de parâmetros do processo FCAW-G nas características da solda do aço ASTM A-36. 2010. 78 f. Dissertação (Mestrado em Engenharia Mecânica e de Materiais) - Universidade Tecnológica Federal do Paraná, Curitiba, 2010. |
| Resumo: | Esta pesquisa tem por finalidade analisar a influência de parâmetros do processo de soldagem com arame tubular com proteção gasosa (Gás Shielded Flux Cored Arc Welding - FCAW-G) nas características da solda do aço ASTM A-36. Parâmetros como tensão do arco (V), velocidade de alimentação do arame (Valim) e distância bico de contato-peça (DBCP) foram variados a fim de detectar suas influências sobre a largura, a penetração, o reforço do cordão e a dureza do metal de solda. Além disso, foi determinada a influência desses parâmetros na taxa de deposição do material de adição, sendo ensaiadas, as soldas, quanto às resistências à tração e ao impacto (ensaio Charpy criogênico) para determinar a qualidade recomendada por norma. As medições geométricas dos cordões de solda foram realizadas em macrografias obtidas da seção transversal da solda, por meio de microscópio óptico, bem como as análises da microestrutura. As medições de dureza foram realizadas com durômetro na seção transversal dos cordões. A taxa de deposição, em kg/h, foi determinada pela pesagem dos corpos-de-prova antes e depois da deposição da solda. Verificou-se que, de forma geral, a morfologia do cordão (largura, penetração e reforço) foi grandemente influenciada pela velocidade de alimentação do arame, seguida pela tensão de soldagem e pela distância bico de contato-peça. Da mesma maneira, a taxa de deposição foi influenciada diretamente pela velocidade de alimentação, pela tensão e pela DBCP: a primeira, com um acréscimo significativo (24,08%); a tensão de forma não muito intensa (4,17%). Desta maneira é possível afirmar, com base nos valores dos parâmetros utilizados neste trabalho, que a maior taxa de deposição (4,32 Kg/h), a melhor morfologia do cordão de solda e dureza adequada foram obtidas com Valim de 12,5 m/min, tensão de 34 V e DBCP de 16 mm. |
| Abstract: | This research aims to analyze the influence of the parameters of Gas Shielded Flux Cored Arc Welding (FCAW-G) on the characteristics of welding steel ASTM A-36. Parameters such as arc voltage (V), feed speed of the wire (Valim) and stickout (distance nozzle contact piece - DBCP) were varied to detect their influence on the width, penetration, reinforcement of the cord, and the hardness of metal weld. Furthermore, it was determined the influence of these parameters on deposition rate of filler metal and the welds were tested for resistance to tensile and impact strength (Charpy test) to determine the quality of the recommended standard. The geometric measurements of weld were carried out in macrographs by the obtained from the cross section of the weld, through an optical microscope as well as the analysis of the microstructure. The hardness measurements were carried out with durometer in cross section of the fillets. The deposition rate in kg/h was determined by weighing the specimen before and after the deposition of solder. It was found that in general the morphology of the cord (width, penetration and reinforcement) was greatly influenced directly by the feed speed of the wire, followed by welding voltage, and stickout. Similarly, the deposition rate was directly influenced by the feed speed, voltage and DBCP, the first with a significant increase (24, 08%), and the tension witch a not so intensive effect (4, 17%). Thus it can be said based on the values of the parameters used in this study that the highest rate of deposition (4,32 kg/h), the better morphology of the weld cord and appropriate hardness was obtained with Valim of 12.5 m/min, voltage 34 V and 16 mm DBCP . |
| Descrição: | Este trabalho foi desenvolvido no programa de Mestrado Interinstitucional - MINTER - entre a UTFPR e o IFAM, com financiamento da Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES - através do projeto ACAM 1379/2006 e da Superintendência da Zona Franca de Manaus - SUFRAMA - através do convênio 084/2005. |
| URI: | http://repositorio.utfpr.edu.br/jspui/handle/1/181 |
| Aparece nas coleções: | CT - Programa de Pós-Graduação em Engenharia Mecânica e de Materiais |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| CT_PPGEM_M_Rodrigues, Emanuel Rezende_2010.pdf | 2,04 MB | Adobe PDF |  Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.